A continuing analysis of the pressurized-thermal-shock problem associated with PWR postulated overcooling accidents indicates that the previously accepted degree of conservatism in the fracture-mechanics model needs to be more closely evaluated, and, if excessive, reduced. One feature that was believed to be conservative was the use of two-dimensional as opposed to finite-length (three-dimensional) flaws. The degree of conservatism could not be adequately investigated because of computational limitations and a lack of knowledge regarding flaw behavior; however, that situation has changed to the extent that some cases involving finite-length flaws can be studied. A flaw of particular interest is one that is located in an axial weld of a plate-type vessel. For those vessels that suffer relatively high-radiation damage in the welds, the length of the flaw will be no greater than the length of the weld, and recent calculations indicate that a deep flaw of that length (∼2 m) is not effectively infinitely long, contrary to previous thinking. The benefit to be derived from consideration of the 2-m flaw and also a semi-elliptical flaw with length-to-depth ratio of 6/1 was investigated by analyzing several postulated transients. In doing so the sensitivity of the benefit to a specified maximum crack-arrest toughness and to the duration of the transient was investigated. Results of the analysis indicate that for some conditions the benefit in using the 2-m flaw is substantial, but it decreases with increasing pressure, and above a certain pressure there may be no benefit, depending on the duration of the transient and the limit on crack-arrest toughness.
Skip Nav Destination
Article navigation
November 1984
Research Papers
A Reassessment of PWR Pressure Vessel Integrity During Overcooling Accidents, Considering 3-D Flaws
R. D. Cheverton,
R. D. Cheverton
Oak Ridge National Laboratory, Oak Ridge, Tenn. 37831
Search for other works by this author on:
D. G. Ball
D. G. Ball
Oak Ridge National Laboratory, Oak Ridge, Tenn. 37831
Search for other works by this author on:
R. D. Cheverton
Oak Ridge National Laboratory, Oak Ridge, Tenn. 37831
D. G. Ball
Oak Ridge National Laboratory, Oak Ridge, Tenn. 37831
J. Pressure Vessel Technol. Nov 1984, 106(4): 375-382 (8 pages)
Published Online: November 1, 1984
Article history
Received:
July 26, 1984
Online:
November 5, 2009
Article
Article discussed|
View article
Connected Content
Citation
Cheverton, R. D., and Ball, D. G. (November 1, 1984). "A Reassessment of PWR Pressure Vessel Integrity During Overcooling Accidents, Considering 3-D Flaws." ASME. J. Pressure Vessel Technol. November 1984; 106(4): 375–382. https://doi.org/10.1115/1.3264367
Download citation file:
Get Email Alerts
Cited By
Research on the Accelerated Life Test Method for Gaskets and the Verification of the Accuracy of the Life Prediction
J. Pressure Vessel Technol (June 2025)
Optimization of High-Vapor Pressure Condensate Pipeline Commissioning Schemes in Large Uplift Environments
J. Pressure Vessel Technol (June 2025)
Related Articles
Deterministic and Probabilistic Fracture Mechanics Analysis for Structural Integrity Assessment of Pressurized Water Reactor Pressure Vessel
J. Pressure Vessel Technol (June,2016)
Probability of Fracture for HFIR Pressure Vessel Caused by Random Crack Size or by Random Toughness
J. Pressure Vessel Technol (February,1994)
CFD Tool for Assessment of the Reactor Pressure Vessel Integrity in Pressure Thermal Shock Conditions: Influence of Turbulence Model and Mesh Refinement on the Vessel Thermal Loading During PTS Transient
J. Pressure Vessel Technol (June,2011)
Application of the Failure Assessment Diagram to the Evaluation of Pressure-Temperature Limits for a Pressurized Water Reactor
J. Pressure Vessel Technol (May,1985)
Related Proceedings Papers
Related Chapters
Development of Nuclear Boiler and Pressure Vessels in Taiwan
Companion Guide to the ASME Boiler and Pressure Vessel Code, Volume 3, Third Edition
Applications of Elastic-Plastic Fracture Mechanics in Section XI, ASME Code Evaluations
Online Companion Guide to the ASME Boiler & Pressure Vessel Codes
Section XI Flaw Acceptance Criteria and Evaluation Using Code Procedures
Online Companion Guide to the ASME Boiler & Pressure Vessel Codes