Cooling helium of high temperature reactors (HTRs) is expected to contain a low level of impurities: oxidizing gases and carbon-bearing species. Reference structural materials for pipes and heat exchangers are chromia former nickel base alloys, typically alloys 617 and 230. And as is generally the case in any high temperature process, their long term corrosion resistance relies on the growth of a surface chromium oxide that can act as a barrier against corrosive species. This implies that the HTR environment must allow for oxidation of these alloys to occur, while it remains not too oxidizing against in-core graphite. First, studies on the surface reactivity under various impure helium containing low partial pressures of , , CO, and show that alloys 617 and 230 oxidize in many atmosphere at intermediate temperatures (up to , depending on the exact gas composition). However when heated above a critical temperature, the surface oxide becomes unstable. It was demonstrated that at the scale/alloy interface, the surface oxide interacts with the carbon from the material. These investigations have established an environmental area that promotes oxidation. When exposed in oxidizing HTR helium, alloys 617 and 230 actually develop a sustainable surface scale over thousands of hours. On the other hand, if the scale is destabilized by reaction with the carbon, the oxide is not protective anymore, and the alloy surface interacts with gaseous impurities. In the case of -containg atmospheres, this causes rapid carburization in the form of precipitation of coarse carbides on the surface and in the bulk. Carburization was shown to induce an extensive embrittlement of the alloys. In -free helium mixtures, alloys decarburize with a global loss of carbon and dissolution of the pre-existing carbides. As carbides take part in the alloy strengthening at high temperature, it is expected that decarburization impacts the creep properties. Carburization and decarburization degrade rapidly the alloy properties, and thus result in an unacceptably high risk on the material integrity at high temperature. Therefore, the purification system shall control the gas composition in order to make this unique helium atmosphere compatible with the in-core graphite, as well as with structural materials. This paper reviews the data on the corrosion behavior of structural materials in HTRs and draws some conclusions on the appropriate helium chemistry regarding the material compatibility at high temperature.
Skip Nav Destination
e-mail: celine.cabet@cea.fr
e-mail: fabien.rouillard@cea.fr
Article navigation
November 2009
Research Papers
Corrosion Issues of High Temperature Reactor Structural Metallic Materials
Celine Cabet,
Celine Cabet
CEA, DEN, DPC, SCCME,
e-mail: celine.cabet@cea.fr
Laboratoire d’Etude de la Corrosion Non Aqueuse
, F-91191 Gif-sur-Yvette, France
Search for other works by this author on:
Fabien Rouillard
Fabien Rouillard
CEA, DEN, DPC, SCCME,
e-mail: fabien.rouillard@cea.fr
Laboratoire d’Etude de la Corrosion Non Aqueuse
, F-91191 Gif-sur-Yvette, France
Search for other works by this author on:
Celine Cabet
CEA, DEN, DPC, SCCME,
Laboratoire d’Etude de la Corrosion Non Aqueuse
, F-91191 Gif-sur-Yvette, Francee-mail: celine.cabet@cea.fr
Fabien Rouillard
CEA, DEN, DPC, SCCME,
Laboratoire d’Etude de la Corrosion Non Aqueuse
, F-91191 Gif-sur-Yvette, Francee-mail: fabien.rouillard@cea.fr
J. Eng. Gas Turbines Power. Nov 2009, 131(6): 062902 (6 pages)
Published Online: July 16, 2009
Article history
Received:
November 3, 2008
Revised:
November 28, 2008
Published:
July 16, 2009
Citation
Cabet, C., and Rouillard, F. (July 16, 2009). "Corrosion Issues of High Temperature Reactor Structural Metallic Materials." ASME. J. Eng. Gas Turbines Power. November 2009; 131(6): 062902. https://doi.org/10.1115/1.3098377
Download citation file:
Get Email Alerts
Experimental Identification Of Blade Tip Rub Forces At Engine Relevant Temperatures And Speeds
J. Eng. Gas Turbines Power
Study Of Tandem Rotor Dual Wake Interaction With Downstream Stator Under Unsteady Numerical Approach
J. Eng. Gas Turbines Power
Experimental Design Validation of a Swirl-Stabilized Burner With Fluidically Variable Swirl Number
J. Eng. Gas Turbines Power (April 2025)
Experimental Characterization of a Bladeless Air Compressor
J. Eng. Gas Turbines Power (April 2025)
Related Articles
Stainless Steels With Improved Oxidation Resistance for Recuperators
J. Eng. Gas Turbines Power (April,2006)
A New Low-Alloy Pearlitic Steel for High-Temperature Service
Trans. ASME (October,1937)
Primary Surface Recuperator Alloy Oxidation: A Comparison of Accelerated Engine Testing to Field Operation
J. Eng. Gas Turbines Power (April,2011)
Long-Term Microturbine Exposure of an Advanced Alloy for Microturbine Primary Surface Recuperators
J. Eng. Gas Turbines Power (May,2009)
Related Proceedings Papers
Related Chapters
E110opt Fuel Cladding Corrosion under PWR Conditions
Zirconium in the Nuclear Industry: 20th International Symposium
Nuclear Components Operating in the Creep Regime
Analysis of ASME Boiler, Pressure Vessel, and Nuclear Components in the Creep Range
The Oxidation of Niobium in the β Phase and Its Impact on the Corrosion of Zr-Nb Alloys under Reactor Conditions
Zirconium in the Nuclear Industry: 20th International Symposium