Isotropic conductive adhesives (ICA) have been considered as replacement materials for lead-tin solder alloys. In this paper, the post-impact shear strength of ICA surface mount (SM) joints was obtained experimentally and compared with that of SM lead-tin joints. The dynamic impact energy was provided in the form of three-point bending on the PCB using equipment called the split Hopkinson bar. Strain rates of over 4000/s were used for the impact bending test. The action of impact bending was used to simulate the effect on the PCB and the interconnection as a result of high energy impact on an electronic equipment. Shear test was then performed to examine the change in strength of the ICA joints as a result of impact damage. It was found that the SM ICA joints failed due to impact at a strain rate just over 4000/s. Microstructural examination carried out using a scanning electron microscope revealed that the interface between the ICA and copper pad on the PCB was the weakest region of the joint.
Skip Nav Destination
e-mail: Lawrence.Wu@cityu.edu.hk
Article navigation
December 2002
Technical Papers
Impact Resistance of SM Joints Formed With ICA
C. M. Lawrence Wu,
e-mail: Lawrence.Wu@cityu.edu.hk
C. M. Lawrence Wu
Department of Physics and Materials Science, City University of Hong Kong, Hong Kong
Search for other works by this author on:
Robert K. Y. Li,
Robert K. Y. Li
Department of Physics and Materials Science, City University of Hong Kong, Hong Kong
Search for other works by this author on:
N. H. Yeung
N. H. Yeung
Department of Physics and Materials Science, City University of Hong Kong, Hong Kong
Search for other works by this author on:
C. M. Lawrence Wu
Department of Physics and Materials Science, City University of Hong Kong, Hong Kong
e-mail: Lawrence.Wu@cityu.edu.hk
Robert K. Y. Li
Department of Physics and Materials Science, City University of Hong Kong, Hong Kong
N. H. Yeung
Department of Physics and Materials Science, City University of Hong Kong, Hong Kong
Contributed by the Electronic and Photonic Packaging Division and presented at Poly 2000, London, United Kingdom, December 4–5, 2000. Manuscript received at ASME Headquarters, May 2002. Guest Editor: Bernd Michel.
J. Electron. Packag. Dec 2002, 124(4): 374-378 (5 pages)
Published Online: December 12, 2002
Article history
Received:
May 1, 2002
Online:
December 12, 2002
Citation
Wu, C. M. L., Li , R. K. Y., and Yeung, N. H. (December 12, 2002). "Impact Resistance of SM Joints Formed With ICA ." ASME. J. Electron. Packag. December 2002; 124(4): 374–378. https://doi.org/10.1115/1.1502666
Download citation file:
Get Email Alerts
Cited By
Enhancing Mechanical Reliability of Silver-Sintered Joints With Copper Nanowires in High-Power Electronic Devices
J. Electron. Packag (December 2024)
Special Issue on InterPACK2023
J. Electron. Packag (December 2024)
Impact of Encapsulated Phase Change Material Additives for Improved Thermal Performance of Silicone Gel Insulation
J. Electron. Packag (December 2024)
Related Articles
Impact Resistance of SM Joints Formed With ICA
J. Electron. Packag (March,2003)
Comparative Strengths of Some Adhesive-Adherend Systems
Trans. ASME (February,1951)
Solid State Bonding of Silver Foils to Metalized Alumina Substrates at 260°C
J. Electron. Packag (December,2011)
A Mechanics of Materials Model for the Creping Process
J. Manuf. Sci. Eng (October,2011)
Related Proceedings Papers
Related Chapters
Impact Testing
A Quick Guide to API 510 Certified Pressure Vessel Inspector Syllabus
In Situ Observations of the Failure Mechanisms of Hydrided Zircaloy-4
Zirconium in the Nuclear Industry: 20th International Symposium
Subsection NF—Supports
Companion Guide to the ASME Boiler & Pressure Vessel Codes, Volume 1 Sixth Edition